| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYETHYLENE – LDPE |
| Grade |
|---|
| 2100TN00 |
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI (200 o c/5kg ) | ISO 1133 | g/10 min | 0.3 |
| Density | ISO 1183 (A) | Kg/m3 | 921 |
| Haze | ASTM D 1003 (A) | % | 15 |
| Clarity | DSM Method | mV | 56 |
| Gloss | ASTM D2457 | % | 39±5 |
| Anti Oxidant | DSM Method | ppm | 600±60 |
| Anti Block | - | ppm | - |
| Slip | - | ppm | - |
| Impact Strength | ASTM D4272 | kJ/m | 35 |
| Tear strength TD | ISO 6383-2 | KN/m | 25 |
| Tear strength MD | ISO 6383-2 | KN/m | 20 |
| Yield Stress TD | ISO R527-1 | MPa | 11 |
| Yield Stress MD | ISO R527-1 | MPa | 12 |
| Tensile strength TD | ISO R527-1 | MPa | 26 |
| Tensile strength MD | ISO R527-1 | MPa | 29 |
| Elongation @ break TD | ISO R527-1 | % | >500 |
| Elongation @ break MD | ISO R527-1 | % | >200 |
| Modulus of elasticity TD | ISO R527-1 | MPa | 190 |
| Modulus of elasticity MD | ISO R527-1 | MPa | 180 |
| Co efficient of friction | ASTM D1894 | - | 0.7 |
| Application |
|---|
| Shrink hoods, Industrial sacks, Carrier bags and liners. |
| Characteristics |
|---|
| Excellent toughness and outstanding biaxial shrink properties, The material contains no additives, has a very low energy consumption during processing, Excellent draw down ability. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYETHYLENE – LDPE |
| Grade |
|---|
| 2102TX00 |
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI | ISO 1133 | g/10 min | 1.9 |
| Density | ISO 1183 (A) | Kg/m3 | 921 |
| Haze | ASTM D 1003 (A) | % | 11 |
| Clarity | DSM Method | mV | 29 |
| Gloss | ASTM D2457 | % | 50±5 |
| Anti Oxidant | DSM Method | ppm | 600±60 |
| Anti Block | - | ppm | - |
| Slip | - | ppm | - |
| Impact Strength | ASTM D4272 | kJ/m | 26 |
| Tear strength TD | ISO 6383-2 | KN/m | 25 |
| Tear strength MD | ISO 6383-2 | KN/m | 60 |
| Yield Stress TD | ISO R527-1 | MPa | 11 |
| Yield Stress MD | ISO R527-1 | MPa | 13 |
| Tensile strength TD | ISO R527-1 | MPa | 20 |
| Tensile strength MD | ISO R527-1 | MPa | - |
| Elongation @ break TD | ISO R527-1 | % | >500 |
| Elongation @ break MD | ISO R527-1 | % | >150 |
| Modulus of elasticity TD | ISO R527-1 | MPa | 200 |
| Modulus of elasticity MD | ISO R527-1 | MPa | 190 |
| Co efficient of friction | ASTM D1894 | - | >1.0 |
| Application |
|---|
| For general purpose film without additives, Used in a wide range of widths and thicknesses for pouches, bags, liners, and lamination film. |
| Characteristics |
|---|
| Is a standard grade produced by the tubular process without additives, Supplied in the form of pellets, in bulk or in 25 kg Bags. The bags are delivered on shrink-wrapped pallets, with a total weight of 1375 kg per pallet. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYETHYLENE – LDPE |
| Grade |
|---|
| 2119 |
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| MFI(190 0C /2 .16 Kg ) | 1.9 | dg/min | ISO1133 |
| Density | 921 | Kg/m3 | ISO 1183 (A) |
| Impact strength | 26 | KJ/m | ASTM D 4272 |
| Tear strength (TD) | 25 | KN/m | ISO 6383-2 |
| Tear Strength (MD) | 60 | KN/m | ISO 6383-2 |
| Yield stress (TD) | 11 | MPa | ISO 527 |
| Yield stress (MD) | 13 | MPa | ISO 527 |
| Tensile stress at break (TD) | 20 | MPa | ISO 527 |
| Tensile stress at break (MD) | 35 | MPa | ISO 527 |
| Strain at Break (TD) | >500 | % | ISO 527 |
| Strain at Break (MD) | >150 | % | ISO 527 |
| Modulus of Elasticity (TD) | 200 | MPa | ISO 527 |
| Modulus of Elasticity (MD) | 190 | MPa | ISO 527 |
| Coefficient of friction | >1 | ASTM D 1894 | |
| Blocking | 20 | g | SABTEC method |
| Re-blocking | 100 | g | SABTEC method |
| Haze | 9 | % | ASTM D 1003A |
| Gloss (45o) | 55 | % | ASTM D 2457 |
| Clarity | 26 | mV |
| Application |
|---|
| Blown film extrusion, Packaging and general lamination films. |
| Characteristics |
|---|
| Excellent optical properties, A high output and excellent draw down and specially designed for general purpose thin films.Properties are based on 25 μm blown film produced at a melt temperature of 170°C and 3 BUR using 100% LFI2119. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYETHYLENE – LDPE |
| Grade |
|---|
| 2420H |
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| Mass Density (23 °C) | 0.924 | g/cm3 | ISO1183 |
| Melt Flow Rate (190°C /2.16kg) | 2 | g/10min | ISO1133 |
| Melting point | 112 | °C | ISO11357 |
| Vicat softening temperature, A/50 | 95 | °C | ISO306 |
| Tensile Modulus of Elasticity | 270 | MPa | ISO527 |
| Stress at Yield | 11 | MPa | ISO527 |
| Shore D hardness | 48 | － | ISO868 |
| Max. tensile strength MD | 23 | MPa | ISO527 |
| Max. tensile strength TD | 21 | MPa | ISO527 |
| Maximum elongation MD | 580 | % | ISO527 |
| Maximum elongation TD | 700 | % | ISO527 |
| Dart Drop Impact | 110 | g | ASTM D1709 |
| Gloss ( 60°) | 120 | － | ASTM D2457 |
| Haze (40μm film) | 6.5 | % | ASTM D1003 |
| Application |
|---|
| Bags & Pouches,Film Shrink, Film Blown Film, Cast Film. |
| Characteristics |
|---|
| Good Heat Seal, Optical, Good Processability. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYETHYLENE – LDPE |
| Grade |
|---|
| 2420D |
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| MFI(190 0C /2 .16 Kg ) | 0.25 | g/cm3 | ISO1133 |
| Mass Density (23 DC) | 0.923 | Kg/m3 | ISO 1183 |
| Melting point | 113 | °C | ISO11357 |
| Vicat softening temperature, A/50 | 95 | °C | ISO306 |
| Tensile Modulus of Elasticity | 260 | MPa | ISO527 |
| Stress at Yield | 10 | MPa | ISO527 |
| Shore D hardness | 48 | ISO868 | |
| Max. tensile strength MD | 25 | MPa | ISO527 |
| Max. tensile strength TD | 24 | MPa | ISO527 |
| Maximum elongation MD | 600 | % | ISO527 |
| Maximum elongation TD | 650 | % | ISO527 |
| Dart Drop Impact | 270 | g | ASTM D1709 |
| Gloss ( 60°) | 100 | － | ASTM D2457 |
| Haze (40μm film) | 8.5 | % | ASTM D1003 |
| Application |
|---|
| Bags & Pouches, Film, Shrink Film, Bottles for Consumer Goods, Blown Film. |
| Characteristics |
|---|
| Good Processability, Good Tear Strength, Good Toughness. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYETHYLENE – LDPE |
| Grade |
|---|
| LH0075 |
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI (190 C/2. 16 kg) | ASTM D 1238 | gr/10 min | 0.75 |
| Density | TSTM 209 B | gr/ml | 0.921 |
| Vicat softening point | ASTM D 1525 | C | 94 |
| Elongation @ break (MD) | ASTM D882 | % | 300 min. |
| Elongation @ break (TD) | ASTM D 882 | % | 450 min. |
| Tensile @ break (MD) | ASTM D 882 | kg/cm2 | 170 min |
| HDT | ASTM D 648 | oC | 33 |
| Dart impact | ASTM D 1709 | gr | 120 min |
| Application |
|---|
| Combining good flexible extrusion behavior and superior mechanical properties, High dart impact combined with excellent yield and tensile strength and high Stiffness, can be processed on automatic machines, possesses good dimensional stability. |
| Characteristics |
|---|
| Carrier bags, Shrink film & industrial film, Dust bin liners, Large bottles, Blow moulding of small containers, Packaging of pharmaceutical products and Foodstuffs, Bottles for storage of chemical products. |
| Packaging |
|---|
| 25 Kg plastic bag |