Also known as polypropylene, is a thermoplastic polymer used in a wide variety of applications including packaging and labeling, textiles (e.g., ropes, thermal underwear and carpets), stationery, plastic parts and reusable containers of various types, laboratory equipment, loudspeakers, automotive components, and polymer banknotes. An addition polymer made from the monomer propylene, it is rugged and unusually resistant to many chemical solvents, bases and acids. Properties : Rigid, Opaque, Good dimensional stability at high temperature and humidity conditions, Tough.
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| 552 R |
| PROPERTY | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (230 oC, 2.16kg) | 25 | g/10min | ASTM D1238 |
| Rockwell Hardness | 100 | R.Scale | ASTM D785 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Tensile Strength at Yield | 32 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 13 | % | ASTM D638 |
| Izod Impact Strength (notched) at 23 oC | 30 | J/m | ASTM D256 |
| Vicat softening point (10N) | 152 | oC | ASTM D1525 |
| H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
| Application |
|---|
| Handkerchiefs and handkerchiefs, Straps for backpacks, sports bags, bulk bags and seat belts, Upholstery and sportswear, Bulk continuous filament for carpets, Nonwoven staple fiber, Injection molded products, household items. |
| Characteristics |
|---|
| Excellent anti gas fading properties, High melt flow, Good workability Homopolymer. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| L H3150-02.0 |
| Property | Unit | Value |
|---|---|---|
| Melt flow rate | (230°C / 2.16 kg), kg/ 10min) | 2,1-2,9 |
| Density | kg/sm3 | 0.90-0,91 |
| Tensile yield strength | at 50 mm/min,MPa | 32 MPa |
| Tensile elongation at yield | at 50mm/min, % | 7,6 |
| Flexural modulus | (1% secant), at 1.4 mm/min, MPa | 1360 |
| Notched Izod impact strength | at 23°C, J/m | 34 J/m |
| Application |
|---|
| Uses for Packaging and Extrusion is used in thermoforming and extrusion blow molding processes. |
| Characteristics |
|---|
| Consistent workability, Good melt strength, High hardness, High strength properties. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| LH5088-25G.O |
| Property | Unit | Value |
|---|---|---|
| Melt flow rate | (230°C / 2.16 kg), g/ 10min) | 21,0-29,0 |
| Density | kg/sm3 | 0.90-0,91 |
| Tensile yield strength | at 50 mm/min,MPa | 33 |
| Tensile elongation at yield | at 50mm/min, % | 6,6 |
| Flexural modulus (1% secant) | at 1.4mm/min, MPa | 1360 |
| Notched Izod impact strength | at23°C, J/m | 18 |
| Application |
|---|
| Uses in bulk continuous fiber processes, from which fibers are used to produce face yarn for carpet. |
| Characteristics |
|---|
| Consistent processibility, Anti-gas fading properties, High speed processing, High strength properties. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| LH3066-03.0 |
| Property | Unit | Value |
|---|---|---|
| Melt flow rate | (230°C / 2.16 kg), g/ 10min) | 2,9-3,9 |
| Density | kg/sm3 | 0.90-0,91 |
| Tensile yield strength | at 50 mm/min,MPa | 29 |
| Tensile elongation at yield | at 50mm/min, % | 8,6 |
| Flexural modulus (1% secant) | at 1.4mm/min, MPa | 1190 MPa |
| Notched Izod impact strength | at 23°C, J/m | 34 |
| Application |
|---|
| Uses in biaxially oriented (BOPP) processes, As a resin for snack/bakery laminations, Overwrap or metallized film applications. |
| Characteristics |
|---|
| Consistent processibility, Good optical properties, High strength properties. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| L R7175-35.P |
| Property | Unit | Value |
|---|---|---|
| Melt flow rate | (230°C / 2.16 kg), g/ 10min) | 30,0-40,0 |
| Density | kg/sm3 | 0.885-0,905 |
| Tensile yield strength | at 50 mm/min,MPa | 25 |
| Tensile elongation at yield | at 50mm/min, % | 7,6 |
| Flexural modulus (1% secant) | at 1.4mm/min, MPa | 935 |
| Notched Izod impact strength | at 23°C, J/m | 29 |
| Application |
|---|
| Uses in injection molding processes, For packaging and consumer housewares applications. |
| Characteristics |
|---|
| Low taste and odor, Good processibility. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| LH5072-03.O |
| Property | Unit | Value |
|---|---|---|
| Melt flow rate | (230°C / 2.16 kg), g/ 10min) | 3,0-4,0 |
| Density | kg/sm3 | 0.90-0,91 |
| Tensile yield strength | at 50 mm/min,MPa | 33 |
| Tensile elongation at yield | at 50mm/min, % | 7,6 |
| Flexural modulus (1% secant) | at 1.3 mm/min, MPa | 1275 |
| Notched Izod impact strength | at 23°C, J/m | 30 |
| Application |
|---|
| Produce woven fabrics for carpet backing, sacking, industrial, geotextile, and rope and twine applications. |
| Characteristics |
|---|
| Consistent processibility, Good color stability and high strength properties, High speed processing, Low water “carry-over”. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| TPP D30 S |
| Property | Unit | Value |
|---|---|---|
| Volume speed of fluidity | g/10 min | 2,7-3,7 |
| Index of polymeric granules turning yellow | not more than | 2 |
| Dimension of granules | ps/g | 40-60 |
| Uniformity of granules | %, not less than | 50 |
| The elasticity module at a bend | N/mm2, not less than | 1300 |
| Strength at a stretching in a fluidity limit | N/mm2, not less than | 30 |
| Relative lengthening at a stretching in a fluidity limit | %, not less than | 11 |
| Shock durabilityby Изоду (with a cut at 23°C) | kDj/m2 | 4.5 |
| Softening temperature by Vick (10N) | °C, not less than | 145 |
| Temperature of admissible deformation | at 0,46 MPa, °C, not less than | 110 |
| Thermooxidizing stability | at 150°C (in the environment of air), hour,not less than | 360 |
| Definition of number and the sizes of gels in polyolefines, not more than | - Defects >0,2 mm - Defects 0,7-1,5 mm - Defects 1,5-2,5 mm - Defects > 2,5 mm | - |
| Turbidity polyolefine plates and films | - | - |
| Application |
|---|
| Uses to produce monofilament, For the release of brushes and brooms, For other technical applications, Vending machine glasses, dairy products and trays intended for fruit, biscuits, and chocolate, Food packaging and sport equipments. |
| Characteristics |
|---|
| Excellent machinability, Excellent mechanical properties. |
| packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| TPP F 79 FB |
| Property | Unit | Value |
|---|---|---|
| Volume speed of fluidity | g/10 min | 2021-10-15 00:00:00 |
| Index of polymeric granules turning yellow | not more than | 2 |
| Dimension of granules | ps/g | 40-60 |
| Uniformity of granules | %, not less than | 50 |
| The elasticity module at a bend | N/mm2, not less than | 1450 |
| Strength at a stretching in a fluidity limit | N/mm2, not less than | 31 |
| Relative lengthening at a stretching in a fluidity limit | %, not less than | 12 |
| Shock durabilityby Изоду (with a cut at 23°C) | kDj/m2 | 2.5 |
| Softening temperature by Vick (10N) | °C, not less than | 150 |
| Temperature of admissible deformation | at 0,46 MPa, °C, not less than | 130 |
| Thermooxidizing stability | at 150°C (in the environment of air), hour,not less than | 120 |
| Definition of number and the sizes of gels in polyolefines, not more than | - Defects >0,2 mm - Defects 0,7-1,5 mm - Defects 1,5-2,5 mm - Defects > 2,5 mm | - |
| Turbidity polyolefine plates and films | - | - |
| Application |
|---|
| Production of care products for women, patterned fabrics, pads, medical wipes,In the hygiene and medical fields, Uses to produce filters and fibers in the automotive, light and furniture industries. |
| Characteristics |
|---|
| Has excellent spinning ability, Excellent technical ability of sizing fibers, High resistance to fading, Soft, appearance resembling textiles and high tear resistance. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYPROPYLENE |
| Grade |
|---|
| TPP D 382 BF |
| Property | Unit | Value |
|---|---|---|
| Volume speed of fluidity | g/10 min | 2,7-3,7 |
| Index of polymeric granules turning yellow | not more than | 2 |
| Dimension of granules | ps/g | 40-60 |
| Uniformity of granules | %, not less than | 50 |
| The elasticity module at a bend | N/mm2, not less than | 1300 |
| Strength at a stretching in a fluidity limit | N/mm2, not less than | 30 |
| Relative lengthening at a stretching in a fluidity limit | %, not less than | 11 |
| Shock durabilityby Изоду (with a cut at 23°C) | kDj/m2 | 4.5 |
| Softening temperature by Vick (10N) | °C, not less than | - |
| Temperature of admissible deformation | at 0,46 MPa, °C, not less than | - |
| Thermooxidizing stability | at 150°C (in the environment of air), hour,not less than | 360 |
| Definition of number and the sizes of gels in polyolefines, not more than | - Defects >0,2 mm - Defects 0,7-1,5 mm - Defects 1,5-2,5 mm - Defects > 2,5 mm | 500 50 10 0 |
| Turbidity polyolefine plates and films | - | - |
| Application |
|---|
| Food and drug administration, Uses for (manufacture of films) orientable films and cast films. |
| Characteristics |
|---|
| High transparency,High strength, Stability during processing, Excellent dielectric properties. |
| Packaging |
|---|
| 25 Kg plastic bag |