ABS is a terpolymer made by polymerizing styrene and acrylonitrile in the presence of polybutadiene. The proportions can vary from 15% to 35% acrylonitrile, 5% to 30% butadiene and 40% to 60% styrene. The result is a long chain of polybutadiene criss-crossed with shorter chains of poly(styrene-co-acrylonitrile). The nitrile groups from neighboring chains, being polar, attract each other and bind the chains together, making ABS stronger than pure polystyrene.
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYSTYRENE | ABS |
| Grade |
|---|
| SD0150 |
| PROPERTY | TEST METHOD | TEST CONDITION | UNIT | VALUE |
|---|---|---|---|---|
| MFI | ASTM D 1238 | (200ºc/5kg) | Gr/10 min | 1.7 |
| 2 Izod Impact Strength (notched) | ISO 180 | 1/8 inch | Kj / m2 | 25 |
| Tensile Strength @ Yield | ASTM D | 5mm/min | Kgf /cm2 | 440 |
| Elongation @ Break | ASTM D | 5mm/min | % | 40 |
| Flexural Strength @ Yield | ASTM D | 2.8mm/min | Kgf /cm2 | 640 |
| Flexural Modulus | ASTM D | 2.8mm/min | Kgf /cm2 | 20500 |
| Vicat Softening Temperature | ASTM D | 5kg | ºC | 99 |
| Rockwell Hardness | ASTM D | - | R-Scale | 104 |
| Flammability | UL 94 | 1.5mm Specimen | Recognized | HB |
| Application |
|---|
| Auto parts, Home appliances, Electrical parts/ fittings, telecommunication, and electronic devices. |
| Characteristics |
|---|
| Is a rigid thermoplastic with good processing Characteristics, High flow injection molding grade, Considerable impact strength and medium heat deflection. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYSTYRENE – GPPS |
| Grade |
|---|
| GPPS – 1460 |
| PROPERTY | UNIT | VALUE | TEST METHOD |
|---|---|---|---|
| MFI (200oc/5kg ) | g/10 min | 6.5 | ISO 1133 H |
| Styrene residual monomer | PPM | <500 | CLGLABPSG004 (ATOFINA TEST METHOD) |
| Vicat softening point | OC | 103 | ISO 306A50 |
| Rockwell hardness | - | Scale L70 | ASTM D 785 |
| Tensile strength @ break | MPa | 48 | ISO 527-2 |
| Elongation @ break | % | 1 | ISO 527-2 |
| Tensile modulus | MPa | 3200 | ISO 527-2 |
| Refractive index | - | 1.591 | ISO Method |
| Water Absorption | % | <0.1 | ISO 62 |
| Application |
|---|
| Insulation board, Foam sheet of food & fruits trays. |
| Characteristics |
|---|
| It is a high heat resistance and molecular weight crystal polystyrene, Useful in the production of thick sheet by direct inject gassing, Has food contact approval. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYSTYRENE – GPPS |
| Grade |
|---|
| GPPS – 1540 |
| PROPERTY | UNIT | VALUE | TEST METHOD |
|---|---|---|---|
| MFI (200oc/5kg ) | g/10 min | 2.5 | ASTM D 1238 |
| Styrene residual monomer | PPM | <500 | CLGLABPSG004 (ATOFINA TEST METHOD) |
| Vicat softening point | OC | Min101 | ASTM D 1525 |
| Rockwell hardness | - | Scale L70 | ASTM D 785 |
| Tensile strength @ yeild | MPa | - | ASTM D 638 |
| Tensile strength @ break | MPa | 48 | ASTM D 638 |
| Elongation @ break | % | 3 | ASTM D 638 |
| Flexural modulus | MPa | 2900 | ASTM D 790 |
| Tensile modulus | - | 3200 | ASTM D 638 |
| Refractive index | - | 1.591 | ISO Method |
| Water Absorption | % | <0.1 | ASTM D 570 |
| Application |
|---|
| Extrusion: Impact dilution; Gloss layer in co-extrusion; Anionic styrene butadiene copolymer dilution, Packaging articles, Medical applications, Petri dishes, Office equipment, Pen barrels, Crisper boxes, Refrigerators, Cups. |
| Characteristics |
|---|
| An easy flowing crystal polystyrene designed for extrusion or injection Applications, Improves extruder output and thermoforming cycle times when mixed with a super high impact polystyrene. |
| Packaging |
|---|
| 25 Kg plastic bag |
| Product Category |
|---|
| POLYMERS |
| Product Name |
|---|
| POLYSTYRENE | HIPS | 7240 |
| Grade |
|---|
| 7240 |
| PROPERTY | TEST METHOD | UNIT | VALUE |
|---|---|---|---|
| MFI (200 o c/5kg ) | ASTM D 1238 | g/10 min | 4.5 |
| Styrene residual monomer | CLGLABPSG004 (ATOFINA TEST METHOD) | ppm | <500 |
| Vicat softening point | ASTM D 1525 | O C | Min.94 |
| Rockwell hardness | ASTM D 785 | - | Scale |
| Tensile strength @ yeild | ASTM D 638 | MPa | 21 |
| Tensile strength @ break | ASTM D 638 | MPa | 20 |
| Elongation @ break | ASTM D 638 | % | 55 |
| Flexural modulus | ASTM D 790 | MPa | 1750 |
| Tensile modulus | ASTM D 638 | MPa | 1800 |
| Izod impact | ISO 180/1A | % | Min. 8.5 |
| Water absorption | ASTM D 570 | % | <0.1 |
| Application |
|---|
| crystal industrial sheets, Cups and trays, Egg boxes, General packaging, Diluted with crystal for CD inserts, Shoe heels. |
| Characteristics |
|---|
| Is a very high impact polystyrene used in extrusion Industry, The good melt strength of this grade makes it particularly suitable for deep-draw thermoforming. |
| Packaging |
|---|
| 25 Kg plastic bag |